产品说明Product description

·GF-TX2000是一款高性能新型的高分子材料,具有优异的耐磨、耐污耐旧、耐热性能。

·GF-TX2000 is a new kind of high performance polymer material which has excellent wear resistance,stain resistanceold resistance and heat resistance properties.

关键特性Key characteristic

1.表面微亮,手感细腻柔软爽滑A little bright on the surfaceexquisitesmooth and soft touch.

2.粘接强度非常高,可粘接材质:ABS、PC TPU  Very high bonding strengthadhesive materials:ABSPCTPU.

3.超磨高强度,高回复性,抗变形Excellent wear resistance and deformation resistance,high strength and resilience.

4.成型快、不粘模具Rapid molding,non-stick mold.

功能Function

产品应用

Main application

智能腕带Smart bracelet

手机保护套Phone protective cover

仪器外壳Instrument shell

电子器件粘胶配件Electronic plastic accessories

加工方法Processing method

注塑、挤出成型Injection and extrusion molding

环保认证

Environmental certification

ROHS

REACH

EN71-3

PAHS

ASTM-F963

Phthalate

颜色Color

黑色 Black

气味Smell

少许树脂味little resin smell

外型Appearance

圆球形小颗粒Cylindrical particleabout 3mm×1.5mm

储藏期Storage period

常温下通风干燥,24个月Ventilated dry at normal temperature,about 24 months

包装方式Packaging method

25公斤/袋 25kg/bag

物理性能Physical properties

结果Result

单位Unit

方法Method

成型条件Molding condition

比重Specific gravity

1.17±0.02

g/cm3

ASTM D792

干燥温度Drying temp     90 

硬度Hardness

75±5

shoreA

ASTM D2240

干燥时间Drying time      2h

拉伸强度Tensile strength

>10

Mpa

ASTM D412

射嘴温度Nozzle temp     190

断裂延伸Elongation at break

>500

%

ASTM D412

螺筒一段温度Screw 1 temp 180

撕裂强度Tearing strength

>45

Kn/m

ASTM D624

螺筒二段温度Screw 2 temp 170

熔融指数Melt index

>6

g/10min

ASTM D1238

螺筒三段温度Screw 3 temp 170

注意事项Matters need attention

清洗料管

Purge compound

需使用PP或 PE清洗干净机台螺杆,且把机台射嘴彻底清除干净Please make sure you that you have cleaned the machine screw with PP or PE, and put the machine nozzle thoroughly clean.

着色

Coloring

 

 

请选择以PEEVA为基材之色母,切勿使用以PVC为基材者。另外加工时请采用较高的螺杆转速和较高的背压,才能让着色剂达到较好的分散效果Please select color master batch on PE or EVA material with the exception of PVC.Higher screw speed and backpressure are needed for better colorant dispersion.

回收

Recycling

二次料(水口料)回收比率建议zui多10%.

Consistent regrind usage of up to 10% is permissible.